Fire-o Fire Proofing Chemicals by Innotra

	See Fire-O in Action Home Page » What is Fire-O?

Treated Pine (4 x 8 cm)

	Watch the Movie
	Low Quality (9,550 Kb)
	High Quality (27,150 Kb)

Please right click the links above and then select save target as option to downoad the movies.

Test Ref: OSB–01

Treated OSB (8mm thickness –60 * 120mm dimensions)

Test Ref: OSB–01

Treated OSB (8mm thickness –60 * 120mm dimensions)

0 sec

60 sec

120 sec

180 sec

240 sec

300 sec

In test OSB-01, 2 OSB pieces, subject to blowtorch flame (1300^oC) untreated piece starts showing deformations by the 2nd minute. By the 5th minute, it burrns to ashes. The treated piece, by the end of the 5th minute shows minor deformation, never catches fire and there is minor carbonization at the back side proving that the treated piece does not conduct heat either.

	Watch the Movie
	Low Quality (2,632 Kb)
	High Quality (16,187 Kb)

Please right click the links above and then select save target as option to downoad the movies.

Test Ref: OSB–02

Treated OSB (8mm thickness –60 * 120mm dimensions)

0 sec

60 sec

120 sec

0 sec

300 sec

OSB Pieces dipped into gasoline Round #3

OSB Pieces dipped into gasoline Round #4

0 sec

160 sec

0 sec

180 sec

OSB Pieces subject to blowtorch flame

90 sec

240 sec

270 sec

In test OSB-02 A piece of OSB was dipped in gasoline 4 times and the same piece was subjected to blowtorch flame (1300^oC). The first round of the gasoline test was made with a piece of same specs as a comparison. In the following rounds, it was seen that after gasoline burns and evaporates, the fire ceases (in 2,5 -3 sec). OSB piece does not catch fire. It does not get deformed. After the 4th round with gasoline, we have applied blowtorch flame for 4,5 minutes. The piece has been carbonized, never caught flame and

	Watch the Movie
	Low Quality (2,508 Kb)
	High Quality (13,392 Kb)

Please right click the links above and then select save target as option to downoad the movies.

Test Ref: COT–01

Treated Cotton piece of 50 mm diameter

0 sec

30 sec

45 sec

Front

Back

Front

Back

60 sec

75 sec

120 sec

Front

Back

Front

Back

Front

Back

A piece of cotton, treated with Fire-O Fire Proofing Chemicals, has been subjected to blowtorch flame (1300^oC) for 2 minutes. It has been vithnessed that during the test cotton did not take flame and due to the fact that Fire-O gives a non conductivity of heat, the back side of the cotton had moderate carbonization and minor deformation.

	Watch the Movie
	Low Quality (544 Kb)
	High Quality (3,014 Kb)

Please right click the links above and then select save target as option to downoad the movies.

Test Ref: PINE–01

Untreated/Treated Pine (5mm thickness – 40 * 140mm dimensions)

0 sec

30 sec

60 sec

120 sec

150 sec Back

A piece of pine wood, treated with Fire-O, after being subjected to blowtorch flame (1300^oC) is compared to a natural one. The untreated piece burns to ashes in 150 seconds however the treated piece shows minor deformation and the back side preserves its natural color and form.